"shock absorber rod"

Steam treatment Front Shock Base Valve With slope 0.20 for various cars Test equipment we have: 1.Carbon selfur determinator 2.Metallurgic microscope 3.Hydraulic universal material tester 4.Hardness testers 5.Pneumatic measuring instrument 6.Measuring projector 7.Gear testing instrument 8.Electrical profilometer 9.CMM and others Specifications: Inspection machines Projector, CMM, hardness tester, roughness tester, salt spray tester, tensile strength tester, caliper,

Ra 3.2-25 Precision Shock Base Valve , OEM Car powdered metal parts Applicable Material: Carbon steel, Low Carbon steel, middle carbon steel, G35, G45, WCB, WCA, WCC, ISO 340-550, Alloy Carbon steel: G25CrMo4, Heat Resistant Steel, Stainless Steel: CF8, CF8M, . G-X6CrNiMo1810, G-X7CrNiNb1189, SUS 304, 304L, 316, 316L.OR According to customer requirement Copper alloy Brass: HPb59-1, CuZn39Pb1/2/3, CuZn40, C36000, C37710, C67400, etc. Aluminum Bronze: QAl11-6-6, CuAl10Fe2/3,

Surface hardness HRB65 - 95 Shock Base Valve metal powder products with MPIF FC-0208 Powder Compaction Molding Copper alloy Iron alloy Hard metal alloy Powder compaction is the process of compacting metal powder in a die through the application of high pressures. Typically the tools are held in the vertical orientation with the punch tool forming the bottom of the cavity. The powder is then compacted into a shape and then ejected from the die cavity. In a number of these

perfect appearance foot valve via continuous furnace reach proper hardness Specifications: Material Iron base steel Brass base steel According to customer drawing Surface treatment Sand Blasting Zinc/Chrome Plating Rust-preventive treatment (steaming treating) Painting Electrophoresis Powder Coating Description: Product Name: Shock Absorber base valve, foot valve Raw Materials MPIF FC-0208 Feature 1. Density from 6.5-6.7 g/cm3 2. Hardness: HRB 60-100 3. Steam treatment: 2H

perfect appearance foot valve via continuous furnace reach proper hardness Specifications: Material Iron base steel Brass base steel According to customer drawing Surface treatment Sand Blasting Zinc/Chrome Plating Rust-preventive treatment (steaming treating) Painting Electrophoresis Powder Coating Description: Product Name: Shock Absorber base valve, foot valve Raw Materials MPIF FC-0208 Feature 1. Density from 6.5-6.7 g/cm3 2. Hardness: HRB 60-100 3. Steam treatment: 2H

FC - 0208 Base Valve Shocks By Powder Metallurgy And Sintering Process Name: NINGBO OEM Powder Metallurgy Foot valve Parts With TS16949 Material: Stainless steel, Iron, Brass, Aluminum Alloy, Carbon steel, Alloy steel, or follow your samples & drawings on materials. Tolerance: according to technic demand Inspection: 100% inspection before shipment Application: shock absorber Monthly capacity: 500000pcs MOQ: 1000pcs Samples: Samples are available in stock Packing: Carton,

wide groove powder metal piston assemble PTFE bands in car shock absorber Specifications: Material P/M Copper and Copper Alloys P/M Iron and Carbon Steel Iron And Carbon Steel Iron-Copper And Copper Steel Sinter Hardened Steel Commix Low Alloy Steel Surface treatment Sand Blasting Zinc/Chrome Plating Rust-preventive treatment (steaming treating) Painting Electrophoresis Powder Coating Description: XIAYI produces different kinds of sintered part. These sintered parts include

Alloy powder good tolerance shock base valve density 6.6 g/cm3 without steam treatment Specifications: Density 6.2-6.8 g/cm3 Hardness HRB 45-65 Steam treatment 2H high temp steam holding time Thickness of Fe3O4 0.004-0.005mm Description: HRB45-65 Iron-Copper and Copper Steel Sintered Parts for car shock absorbers Our company produces different kinds of sintered parts. These sintered part include pistons, foot valve, rod guider, valve base and so on. Dimension: D32.5XD6X11.5

Popular Heavy Duty Shock Base Valve with Rust Preventive Export to Europe Market Manufacturability 1.Auto Mechanical Press:50T, 100T, 140T 2.Hydraulic Press:100T, 315T, 600T, 800T 3.Six sinter furnaces, including one harden Sinter Furnace 4.In-house tooling making:EDM, wire cutting machine Specifications: Density 6.2-6.8 g/cm3 Hardness HRB 45-65 Steam treatment 2H high temp steam holding time Thickness of Fe3O4 0.004-0.005mm Description: HRB80-100 Iron-Copper and Copper Steel